Hardness Guaranteed [HBW] Impact energy guaranteed Min [J] Yield strength Rp0.2 [MPa]* Tensile strength Rm[MPa]* Elongation As [%]* Compressive strength Rc0.2[MPa]* Impact energy [J] Plate Thickness [mm] Bar Diameter [mm]
Toolox 33 - A quenched and tempered tool steel designed to have low residual stresses - resulting in good dimensional stability.
-40°C 27 6-130 21-141
-20°C 45
20°C 275-325 35 850 980 16 800 100
200°C 800 900 12 750 170
300°C 700 180
400°C 590 180
500°C 560

Plates are tested in borth longitudinal and transverse direction.
Bars are tested in longitudinal direction.

Hardness Guaranteed [HBW] Impact energy guaranteed Min [J] Yield strength Rp0.2 [MPa]* Tensile strength Rm[MPa]* Elongation As [%]* Compressive strength Rc0.2
[MPa]*
Impact energy [J] Approximate Hardness [HRC]* Rc0.2[MPa] after 170 hrs soaking time at the actual temperature* Plate Thickness [mm] Bar Diameter
Toolox 44 - A quenched and tempered tool steel with very low residual stresses. In spite of a hardness of 45 HRC it boasts very good machinability and is unmatched on the market.
-40°C 14 6 - 130 21 - 141
-20°C 19
20°C 410-475 18 1300 1450 13 1250 30 45
200°C 1200 1380 10 1120 60
300°C 1120 80
400°C 1060 80 1060
500°C 930 910

Plates are tested in borth longitudinal and transverse direction.
Bars are tested in longitudinal direction.
The typical testing temperature for Toolox is room temperature.
All other values are tested randomly and they are for information only.
* Values are for guidance only.